- - - - Time at this new temp causes unstable \(\gamma\) to release \(\gamma'\)
      - \(\gamma'\) develops heterogenerously
  - - - If temp is close to transition between \(\gamma\) and \(\gamma +\gamma'\) then few large nuclei
      - As temp moves away from transition then more smaller nuclei