- - - - Warna
      - Transluence
      - Fluorescence
- - - - untuk reaksi asam basa
    - - memperpanjang setting time
  - - - kisaran 2-35 nanometer
    - - mempermudah melihat area tumpatan
    - - antara 90-140 mPa
  - - - Tipe III
        
        Linear dan basis
      - Tipe II
        
        Restorasi Estetik (IIa)
        
        Restorasi Reinforced (IIb)
      - Tipe I
        
        Luting Cement
      - Tipe IV
        
        Fissure Sealant
      - Tipe V
        
        Semen Ortodonti
      - Tipe VII
        
        Fluoride Release
      - Tipe VI
        
        Core build up
      - Tipe VIII
        
        Atraumatic Restorative Technique
      - Tipe IX
        
        Restorasi Gigi Sulung
    - - High Viscosity
      - Resin-modified
      - Metal Reinforced
      - Calcium Aluminate
- - - - dilakukan pembilasan etsa
      - tahapan
        
        Aplikasi acid etchant
        
        Aplikasi primer yang mengandung monomer hidrofilik
        
        Apilasi bonding agent
    - - tidak ada pembilasan etsa
      - tahapan
        
        aplikasi monomer asam
        
        aplikasi mid/strong self-etch adhesive
  - - - self-etching primer
        
        acidic monomer
      - monomer hidrofilik
        
        aseton atau alkohol
    - - Air
        
        mengionisasi monomer asam
      - Aseton
      - Alkohol
    - - berikatan dengan dentin primer
    - - inorganic acid
        
        phosphoric acid
      - polymeric acid
        
        poly acrylic acid
      - organic acid
        
        tartaric acid
    - - partikel silica ukuran nanometer
    - - Photoinitiator System
        
        Photosensitizer
        
        Initiator
      - Self-cure system
      - Dual-cure system
    - - Desensitizer
        
        Dentsply
      - Antimikroba
        
        Parabene
- - - - campuran monomer dimethacrylate aromatik atau alifatik
        
        bis-GMA dan urethane dimethacrylate
    - - 30-70% volume
      - 50-85% berat komposit
    - - membentuk matriks resin
    - - camphorquinon
  - - - Hybrid composite
        
        untuk incisal site
      - Nanofilled composite
        
        daya poles unggul
      - microfilled composite
        
        sulit dimanipulasi
      - fine particle composite
        
        cocok pada gigi anterior
    - - Flowable Composite
        
        restorasi kelas I
        
        sifat
        
        viskositas rendah
      - Condensable composite
        
        bahan restorasi
        
        manipulasi susaj
    - - Self-curing
        
        2 pasta
        
        basis dan katalis
        
        powder
        
        inorganik pase + inisiator
        
        liquid
        
        bis-GMA + monomer
      - Light Curing
        
        mengggunakan visible blue light
      - Dual-cured resins
  - - - working dan setting time
        
        light cure: 20-60 detik
        
        self-cure: 3-5 menit
      - Water sorption
      - Thermal properties
        
        memicu pembentukan celah
      - polymerization shrinkage
        
        tekanan polimerisasi
    - - Solubility
        
        resin memiliki penyerapan lebih besar
      - Color stability
        
        tahan terhadap perwarnaan
    - - Biokompatibilitas
      - Wear Rates
        
        nanokomposit wear resistence tertinggi