Why does the built sample increase in strength?
Maybe the elements are coming out of solution?
Maybe the precipitates are becoming finer
Testing
Testing with x-ray diffraction
Testing built sample
Gonion testing with divergent beam optics
Found many peaks and was unable to map peaks
Refine Optics
Parallel Beam Optics
Parallel Beam Optics + Monochromoter
Electron Microscopy
uXRD testing
Testing original foil sample
On 65 degrees - 100 steps
Testing built sample
Gonio scan with divergent beam optics
On 62.5 degrees - 100 steps
SEM EDS on voids shows higher oxygen concentration in voids
Testing original foil
BSE EDS shows precipitates
BSE EDS shows precipitates